SKAPS TN 330 – GEOCOMPOSITE – METRIC UNITS

Description

SKAPS TN 330 – GEOCOMPOSITE – METRIC UNITS: SKAPS TRANSNET^TM Geocomposite consists of SKAPS Geonet made from HDPE resin with nonwoven polypropylene geotextile fabric heat-bonded on one side or both sides of Geonet.

PROPERTY	TEST METHOD	UNIT	VALUE	VALUE	QUALIFIER
GEONET
Thickness	ASTM D 5199	mm	7.62	7.62	MAV(3)
Carbon Black	ASTM D 4218	%	2.00	2.00	MAV
Tensile Strength	ASTM D 7179	N/mm	13.11	13.11	MAV
Melt Flow	ASTM D 1238(2)	g/10 min	1.00	1.00	Maximum
Density	ASTM D 1505	g/cm3	0.94	0.94	MAV
Transmissivity(1)	ASTM D 4716	m2/sec	8.0 x 10-3	8.0 x 10-3	MAV
GEOCOMPOSITE			200 g/m2	270 g/m2
Ply Adhesion	ASTM D 7005	g/cm	178	178	MAV
Transmissivity(1) DS	ASTM D 4716	m2/sec	TN 330-2-6	TN 330-2-8
			9.0 x 10-4	9.0 x 10-4	MAV
Transmissivity(1) SS	ASTM D 4716	m2/sec	TN 330-1-6	TN 330-1-8
			3.0 X 10-3	3.0 X 10-3	MAV
GEOTEXTILE
Fabric Weight	ASTM D 5261	g/m2	200	270	MARV(4)
Grab Tensile	ASTM D 4632	N	711	1001	MARV
Grab Elongation	ASTM D 4632	%	50	50	MARV
Trapezoid Tear	ASTM D 4533	N	289	400	MARV
CBR Puncture	ASTM D 6241	N	2002	2670	MARV
Water Flow(5)	ASTM D 4491	l/min/m2	5093	4075	MARV
Permittivity(5)	ASTM D 4491	sec-1	1.63	1.26	MARV
Permeability(5)	ASTM D 4491	cm/sec	0.30	0.30	MARV
AOS	ASTM D 4751	mm	0.212	0.180	MaxARV

  Notes: (1) Transmissivity was measured using water at 21 ± 2 ° C (70 ± 4) ° C with a gradient of 0.1 and a confining pressure of 479 kPa between steel plates after 15 minutes. Values may vary with individual labs. DS – Double-Sided, SS -Single Sided (2) Condition 190/2.16 (3) Minimum average value. (4) MARV is statistically defined as mean minus two standard deviations and it is the value that is exceeded by 97.5% of all the test data. (5) At the time of manufacturing. Handling may change these properties. This