SKAPS TRANSNET 350 – GEOCOMPOSITE – METRIC UNITS

SKAPS TRANSNET^TM Geocomposite consists of SKAPS Geonet made from HDPE resin with nonwoven polypropylene geotextile fabric heat bonded on one side or both sides of Geonet

PROPERTY	TEST METHOD	UNIT	VALUE	VALUE	QUALIFIER
GEONET
Thickness	ASTM D 5199	mil	8.38	8.38	MAV(3)
Carbon Black	ASTM D 4218	%	2.00	2.00	MAV
Tensile Strength	ASTM D 7179	lb/in	17.49	17.49	MAV
Melt Flow	ASTM D 1238(2)	g/10 min	1.00	1.00	Maximum
Density	ASTM D 1505	g/cm3	0.94	0.94	MAV
Transmissivity(1)	ASTM D 4716	gal/min/ft (m2/sec)	9.0 x 10-3	9.0 x 10-3	MAV
GEOCOMPOSITE			200 g/m2	270 g/m2
Ply Adhesion	ASTM D 7005	lb/in	178	178	MAV
Transmissivity(1) DS	ASTM D 4716	gal/min/ft (m2/sec)	TN 350-2-6	TN 350-2-8
			1.2 x 10-3	1.2 x 10-3	MAV
Transmissivity(1) SS	ASTM D 4716	gal/min/ft (m2/sec)	TN 350-1-6	TN 350-1-8
			4.0 X 10-3	4.0 X 10-3	MAV
GEOTEXTILE
Fabric Weight	ASTM D 5261	g/m2	200	270	MARV(4)
Grab Tensile	ASTM D 4632	N	711	1001	MARV
Grab Elongation	ASTM D 4632	%	50	50	MARV
Trapezoid Tear	ASTM D 4533	N	289	400	MARV
CBR Puncture	ASTM D 6241	N	2002	2670	MARV
Water Flow(5)	ASTM D 4491	l/min/m2	5093	4075	MARV
Permittivity(5)	ASTM D 4491	sec-1	1.63	1.26	MARV
Permeability(5)	ASTM D 4491	cm/sec	0.30	0.30	MARV
AOS	ASTM D 4751	mm	0.212	0.180	MaxARV

Notes:
(1) Transmissivity was measured using water at 21 ± 2 ° C (70 ± 4) ° C with a gradient of 0.1 and a confining pressure of 479 kPa between steel plates after 15 minutes. Values may vary with individual labs. DS – Double-Sided, SS -Single Sided
(2) Condition 190/2.16
(3) Minimum average value.
(4) MARV is statistically defined as mean minus two standard deviations and it is the value that is exceeded by 97.5% of all the test data.
(5) At the time of manufacturing. Handling may change these properties.